Re: [adatesman] Hardness testing of cam lobes:
Edit Log
|
|
atlnq9
Mar 14, 2009, 3:26 PM
Views: 11109
Registered: Sep 10, 2007
Posts: 111
|
edavidso did a good explanation, sorry I must have skipped over your post rschap. Only one thing I would say though just for giggles is one could argue that hardening steel and hardening aluminum are really the same they just get contributions from different mechanisms. But that is for another day.
Aric: your ternery, really taking binarys of each side and matching them together to get 3D would be better for seeing...
and this little tid bit, although we consider 6xxx aluminums Al:Mg:Si
Edit: I'll see if I can get you a better more relevant one on monday 